Shengfan Quartz plate characteristic
|
|
|
*Brand
|
shengfanquartz
|
|
*SIO2
|
99.99%
|
|
*Density
|
2.2(g/cm³)
|
|
*Degree of hardness moh’ scale
|
6.6
|
|
*Melting point
|
1732℃
|
|
* Working temperature
|
1100℃
|
|
*Annealing point
|
1180℃
|
|
*Softening point
|
1630℃
|
Setting Information
|
|
|
Color
|
Transparent
|
|
Shape
|
Circular / Round
|
|
Standard
|
JGS1,JGS2,JGS3
|
|
Material
|
99.99% sio2
|
|
Diameter
|
1-800mm
|
|
Thickness
|
0.2-100mm
|
|
Application
|
Optics quartz windows
|
|
Density
|
6.6
|
|
Light Transmittance
|
>92%
|
|
Hardness
|
Mose 6.5
|
|
Resistance Value
|
1000 times than ordinary glass
|
Density
|
2.2x103 kg/m3
|
Hardness
|
5.5 - 6.5 Mohs' Scale 570 KHN 100
|
Design Tensile Strength
|
4.8x107 Pa (N/m2) (7000 psi)
|
Design Compressive Strength
|
Greater than 1.1 x l09 Pa (160,000 psi)SMD 5730
|
Bulk Modulus
|
3.7x1010 Pa (5.3x106 psi)
|
Rigidity Modulus
|
3.1x1010 Pa (4.5x106 psi)
|
Softening Point
|
1730°C
|
Annealing Point
|
1215°C
|
|
JGS1(ZS-1)
|
JGS2(ZS-2)
|
JGS3(HS)
|
Spectral characteristics
|
180-2500nm
|
200-2500nm
|
260-3500nm
|
The average transmittance
|
90%
|
85%
|
85%
|
Bubble class
|
0
|
2
|
2
|
Birefringence
|
1-2
|
1-2
|
1-2
|
Grain structure
|
1
|
2
|
2
|
Fringe
|
1-2
|
2
|
2
|
Uniformity
|
1-2
|
2
|
2
|
Fluorescence
|
1
|
2
|
2
|
Radiation Performance
|
Does not change clolor
|
Sight discoloration
|
Change color
|